Pengaruh Temperatur terhadap Kekuatan Impak Material Baja ST37 dengan Metode Charpy dan Izod

Authors

  • Jandri Fan Politeknik Negeri Medan
  • Sahat Politeknik Negeri Medan
  • Al Qadry Politeknik Negeri Medan
  • Eka Putra Dairi Boangmanalu Politeknik Negeri Medan
  • Angga Bahri Pratama Politeknik Negeri Medan

DOI:

https://doi.org/10.37338/inovator.v6i2.254

Keywords:

Temperatur, Material Baja, Izod

Abstract

Impact Test can be interpreted as a test that measures the ability of a material to accept impact loads which are measured by the amount of energy required to break the specimen with a swing. The aim of this test is to determine the effect of temperature on the value of energy absorbed by the material and the impact value. The method used in this research is the experimental method, namely the method used to find the effect of temperature on the impact strength of charpy and izod. The results of the charpy and izod impact tests on ST37 Steel specimens prove that there is an influence of temperature on the charpy and izod impact tests. Where the higher the temperature, the higher the energy absorbed and the impact price. Conversely, the lower the temperature, the energy absorbed and the impact price will be lower. In the test results, the lowest energy absorbed in the charpy impact test was 76 J and 22 J in the izod impact test, while the highest energy absorbed in the charpy impact test was 245 J and 114 J in the izod impact test. The lowest impact price in the test was 0.1727 J/mm2 for the charpy impact test and 0.037 J/mm2 for the izod impact test, while the highest impact price in the test was 0.5568 J/mm2 for the charpy impact test and 0.19 J/mm2 for izod impact testing.

References

C. U. Wardani, Y. Samantha, H. Budiman, F. Teknik, and U. Majalengka, “ANALISIS PENGUJIAN IMPAK METODA IZOD DAN CHARPY MENGGUNAKAN,” no. 1, pp. 2–5.

P. Seminar, N. Sains, and T. Doi, “No Title,” pp. 131–137, 2020.

H. Porawati, “Jurnal Inovator Analisis Alat Uji Impak Metode Izod pada Bengkel Politeknik Jambi,” vol. 1, no. 1, pp. 1–5, 2018.

J. Fan, H. T. Saragi, A. B. Pratama, E. Putra, D. Boangmanalu, and A. Qadry, “Pengaruh Temperatur terhadap Kekuatan Impak pada Material Besi Nako 10 mm,” vol. 04, no. 01, 2023.

S. Pranata, T. Husni, and R. Afriany, “EISSN : 2686-5416 TEKNIKA : Jurnal Teknik VOL . 7 NO . 2 PENGARUH VARIASI SUHU TEMPERING 200 o C 400 o C 600 o C TERHADAP KEKERASAN DAN KETANGGUHAN BAJA JIS G4801 SUP 9 Fakultas Teknik Universitas IBA TEKNIKA : Jurnal Teknik VOL . 7 NO . Oktober 2020,” vol. 7, no. 2, pp. 216–224.

M. Z. Prawira and S. J. Sisworo, “PENGARUH PERBEDAAN SUHU TERHADAP KEKUATAN IMPACT ALUMUNIUM 5083 HASIL PENGELASAN TUNGSTEN INERT GAS,” pp. 362–370.

D. P. Kosasih and H. D. Nugraha, “Analisa Pengaruh Temperatur terhadap Impact Al 20xx dan Baja AISI,” vol. 4, no. 2, pp. 31–40, 2020.

H. Sukanto, “Pengaruh Suhu Sintering Terhadap Densitas dan Kekuatan Komposit Plastik - Karet The Influence of Sintering Temperature toward Density and Strength of Plastic-Ruber Composite,” vol. 3, no. 1, pp. 2–6, 2009.

M. Z. M, “Pengaruh temperatur dan bentuk takikan terhadap kekuatan impak logam,” vol. 3.

Hasrin, “Analisa perpatahan baja st 60 yang dikenai beban impak charpy,” pp. 1–4.

M. Nurdin, Z. Muhsin, and B. Anwar, “Pengaruh Temperatur terhadap Kekuatan Impak Sambungan Las Listrik pada Material Besi Plat ST 42,” pp. 35–42, 2016.

H. Purwanto, “Analisis Keakuratan Hasil Uji Impact dengan Metode Izod dan Charpy,” pp. 130–135, 2017.

Downloads

Published

2023-12-18

How to Cite

Jandri Fan, Sahat, Al Qadry, Eka Putra Dairi Boangmanalu, & Angga Bahri Pratama. (2023). Pengaruh Temperatur terhadap Kekuatan Impak Material Baja ST37 dengan Metode Charpy dan Izod. Jurnal INOVATOR, 6(2), 65–69. https://doi.org/10.37338/inovator.v6i2.254

Issue

Section

Artikel