Analisis Pengaruh Parameter Proses Pada Kualitas Las SMAW Baja Paduan Stainless Steel 304
DOI:
https://doi.org/10.37338/inovator.v8i2.519Keywords:
SMAW, Stainless steel 304, Arus Pengelasan, Diameter Elektroda, Jenis KampuhAbstract
This study analyzes the effect of Shielded Metal Arc Welding (SMAW) welding process parameter variations on the quality of welded joints in 304 stainless steel by varying the current (65 A, 75 A, and 95 A), electrode diameter (2.0 mm; 2.6 mm; 3.2 mm), and weld type (I, V, and X). Evaluation is carried out through tensile tests to determine tensile load, stress, and strain, as well as Non-Destructive Test (NDT) dye penetrant method to detect surface defects. Taguchi L27 design is used to analyze the contribution of each parameter to the quality of the joint. The results show that current is the most influential factor on tensile strength, followed by electrode diameter and weld type. The optimal combination is obtained at a current of 95 A, a 3.2 mm electrode, and an X (double V) weld, with an average tensile load of 87.65 kN, a stress of 730.42 MPa, and a strain reaching 100% which shows the best mechanical performance. Overall, this study confirms that proper welding parameter settings are crucial for the mechanical integrity and quality of 304 stainless steel welded joints.
References
Mulyana, Yayan dan Irwan Yusril (2021). Pengaruh Besar Arus Pengelasan SMAW Pada Pengelasan Baja Tahan Karat Austentik Terhadap Kekuatan Tarik & Kekerasan. Program Studi Teknik Mesin, Institut Teknologi Nasional Bandung.
Setyowati, Ayu Vuri, Eriek Wahyu Restu Widodo, Suheni (2016). Analisa Pengaruh Jenis Elektroda Pengelasan SMAW Terhadap Kekuatan Stainless steel 304. Program Studi Institut Teknologi Adhi Tama Surabaya.
International. (2015). Standard Specification for Stainless steel Bars and Shapes (ASTM A276/A276M-15).
Hanggara, Arie Bayu dan Harahap R. Muksin (2019). Pengaruh Posisi Pengelasan SMAW dengan Variasi Posisi Elektroda E3086 Terhadap Kekuatan Impak pada Stainless steel AISI 304. Program Studi Teknik Mesin Fakultas Teknik UISU.
Salim, Victor, Rosehan, Lubis Yamin Sobron (2023). Analisis Dampak Perubahan Arus Pengelasan Terhadap Kekuatan Sambungan Las Pada Material Stainless steel 316. Program Studi Teknik Mesin Fakultas Teknik Universitas Tarumanagara.
Pratama, Yundia Olivian dan Yunus (2024). Analisa Pengaruh Variasi Kuat Arus dan Diameter Elektroda Metode Pengelasan SMAW pada Material Stainless Steel 304 Terhadap Kekuatan Tarik dan Bending. Program Studi Teknik Mesin Fakultas Teknik Universitas Negeri Surabaya.
Sugestian, Rizsaldy M (2019). Analisa Kekuatan Sambungan Las SMAW Vertical Horizontal Down Hand Pada Plate Baja JIS 3131SPHC dan Stainless steel 201 Dengan Aplikasi Piles Transfer di Mesin Thermoforming (Stacking Unit). Program Studi Teknik Mesin Fakultas Teknologi Industri Institut Teknologi Nasional Malang.
Aditia, Nurdin, Ismy Adi Saputra (2019). Analisa Kekuatan Sambungan Material AISI 1050 Dengan ASTM A36 Dengan Variasi Arus Pada Proses Pengelasan SMAW. Program Studi Teknik Mesin Politeknik Negeri Lhokseumawe.
Azis, Abdul Rizal, Suharno, Saputro Herman (2019). Pengaruh Variasi Diameter Elektroda E7018 Terhadap Kekuatan Tarik, Kekerasan, dan Struktur Mikro Pengelasan pada Baja Karbon Rendah Jenis SS400 engan Metode SMAW. Program Studi Teknik Mesin Universitas Sebelas Maret.
Endramawan, Tito, Haris Emin, Dionisius Felix, Prika Yuliana (2017). Aplikasi Non. Destructive Test Penetrant Testing (NDT-PT) Untuk Analisis Hasil Pengelasan SMAW 3G Butt Joint. Program Studi Teknik Mesin Politeknik Negeri Indramayu.
American Welding Society. (n.d.). AWS – American Welding Society.
Mazwan, Mazwan, Satrio Darma Utama, and Ridhani Anita Fajardini. "Investigasi Gaya Potong, Kekasaran Permukaan dan Keausan Pahat Pada Proses Bubut Baja Menggunakan Teknik Pelumasan Minimum Quantity Lubrication (MQL) Berbasis Minyak Nabati." ROTASI 26.2: 15-22.
Zulfadly, dan Ghony Abdul Muhammad (2022). Variasi Ampere Terhadap Kekuatan Tarik Pada Hasil Pengelasan Dengan Posisi Down Hand. Program Studi Teknik Perawatan Alat Tambang Akademi Komunitas Industri Pertambangan Bukit Asam.
Martawati, M. E., Fachrudin, A. R., & Astuti, F. A. F. (2023). Pelatihan Pengelasan SMAW Pada Para Pemuda Oro-Oro Ombo Kecamatan Batu Kota Batu. JPEMAS: Jurnal Pengabdian Kepada Masyarakat.
Purwoko, M. S., Romadhoni, R., & Satria, B. (2021). Pelatihan pengelasan SMAW untuk masyarakat kurang mampu Desa Kuala Alam. Tanjak: Jurnal Pengabdian Kepada Masyarakat.
Agustiarina, Niken dan Putri Primary Nugrahani (2020). Deposisi Lapisan Tipis Polianialin Dengan Metode Elektrokimia. Program Studi Fisika FMIPA Universitas Negeri Surabaya.
Mazwan, Mazwan, and Bambang Dwi Haripriadi. "Analisa Burr Pada Proses End-Milling Baja Karbon Lunak Profil Siku Menggunakan CNC Router." Jurnal Inovator 7 (2024): 5-10.
Downloads
Published
Issue
Section
License
Copyright (c) 2025 Muhammad Siraj Mahfud, Bambang Dwi Haripriadi, Agnes Arum Budiana
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.